Metal oxide film and method for forming metal oxide film

ABSTRACT

A metal oxide film including a crystal part and having highly stable physical properties is provided. The size of the crystal part is less than or equal to 10 nm, which allows the observation of circumferentially arranged spots in a nanobeam electron diffraction pattern of the cross section of the metal oxide film when the measurement area is greater than or equal to 5 nmφ and less than or equal to 10 nmφ.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. application Ser. No.15/879,506, filed Jan. 25, 2018, now pending, which is a continuation ofU.S. application Ser. No. 14/071,932, filed Nov. 5, 2013, now U.S. Pat.No. 9,881,939, which claims the benefit of foreign priority applicationsfiled in Japan as Serial No. 2012-245992 on Nov. 8, 2012, Serial No.2013-016242 on Jan. 30, 2013, and Serial No. 2013-056768 on Mar. 19,2013, all of which are incorporated by reference.

TECHNICAL FIELD

One embodiment of the present invention relates to, for example, asemiconductor device, a display device, a light-emitting device, adriving method thereof, or a manufacturing method thereof. Oneembodiment of the present invention particularly relates to a metaloxide film and a method for forming the metal oxide film. Further, oneembodiment of the present invention relates to a semiconductor deviceincluding the metal oxide film.

Note that a semiconductor device in this specification and the likerefers to any device that can function by utilizing semiconductorcharacteristics, and for example, electro-optical devices, semiconductorcircuits, and electronic devices are all semiconductor devices.

BACKGROUND ART

A technique by which a transistor is formed using a semiconductor thinfilm formed over a substrate having an insulating surface has beenattracting attention. Such a transistor is applied to a wide range ofelectronic devices such as an integrated circuit (IC) and an imagedisplay device (also simply referred to as a display device). As asemiconductor film applicable to the transistor, a silicon-basedsemiconductor material is widely known; moreover, a metal oxideexhibiting semiconductor characteristics (an oxide semiconductor) hasbeen attracting attention as another material.

For example, Patent Document 1 discloses a technique in which atransistor is manufactured using an amorphous oxide containing In, Zn,Ga, Sn, and the like as an oxide semiconductor.

REFERENCE Patent Document

[Patent Document 1] Japanese Published Patent Application No.2006-165529

DISCLOSURE OF INVENTION

One object of one embodiment of the present invention is to provide ametal oxide film including a crystal part.

Another object of one embodiment of the present invention is to providea metal oxide film having highly stable physical properties.

Another object of one embodiment of the present invention is to providea highly reliable semiconductor device including the above metal oxidefilm.

Another object of one embodiment of the present invention is to providea novel semiconductor device. Note that the descriptions of theseobjects do not disturb the existence of other objects. Note that in oneembodiment of the present invention, there is no need to achieve all theobjects. Note that other objects will be apparent from the descriptionof the specification, the drawings, the claims, and the like and otherobjects can be derived from the description of the specification, thedrawings, the claims, and the like.

One embodiment of the disclosed invention is a metal oxide filmincluding a minute crystal part in which periodic atomic arrangement isnot observed macroscopically or long-range order in atomic arrangementis not observed macroscopically. The metal oxide film of one embodimentof the present invention includes a region where a halo patternindicating an amorphous state is observed in a selected-area electrondiffraction pattern of the plane. On the other hand, in a nanobeamelectron diffraction pattern of the cross-section, the halo pattern isnot observed, and spots without directionality, which are different fromspots having regularity that represents crystal parts aligned with aspecific plane, are observed. Specifically, one embodiment of thedisclosed invention is, for example, a metal oxide film having any ofthe following structures.

One embodiment of the present invention is a metal oxide film includinga region where a plurality of circumferentially distributed spots areobserved in a nanobeam electron diffraction pattern of a cross-section.

Another embodiment of the present invention is a metal oxide filmincluding a region where a plurality of circumferentially distributedspots are observed in a nanobeam electron diffraction pattern of across-section, and a halo pattern is observed in a selected-areaelectron diffraction pattern of a plane.

In the above, a measurement area of the selected-area electrondiffraction is preferably greater than or equal to 300 nmφ.

In the above, a measurement area of nanobeam electron diffraction ispreferably greater than or equal to 5 nmφ and less than or equal to 10nmφ. Note that irradiation with an electron beam whose beam diameter isconverged to 1 nmφ can give a nanobeam electron diffraction pattern witha measurement area greater than or equal to 5 nmφ and less than or equalto 10 nmφ.

In the above, it is preferable that the nanobeam electron diffractionpattern be that of a cross-section of a sample which is thinned togreater than 10 nm and less than or equal to 50 nm.

In the above, the metal oxide film preferably includes the crystal partand the size of the crystal part is preferably less than or equal to 10nm. Alternatively, the size of the crystal part is preferably greaterthan or equal to 1 nm and less than or equal to 10 nm.

One embodiment of the present invention is a metal oxide film includinga crystal part which includes a region having the following features:nanobeam electron diffraction with a measurement area greater than orequal to 5 nmφ and less than or equal to 10 nmφ allows the observationof a plurality of circumferentially distributed spots from across-section of the metal oxide film thinned to greater than 10 nm andless than or equal to 50 nm, while spots having regularity thatrepresents crystal parts aligned with a specific plane are observed froma cross-section of the metal oxide film thinned to less than or equal to10 nm.

Any one of the above metal oxide films preferably contains at leastindium, gallium, or zinc.

Another embodiment of the present invention is a method for forming ametal oxide film including a region where a plurality ofcircumferentially distributed spots are observed in a nanobeam electrondiffraction pattern of a cross-section. The metal oxide film is formedby a sputtering method at room temperature in an atmosphere containingoxygen using an oxide target.

In the above method for forming a metal oxide film, partial pressure ofoxygen in the atmosphere is preferably greater than or equal to 33%.

One embodiment of the present invention can provide a metal oxide filmincluding a crystal part.

Further, one embodiment of the present invention can provide a metaloxide film having highly stable physical properties. Furthermore, withthe use of the metal oxide film in a semiconductor device, thesemiconductor device can have high reliability.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1A is a cross-sectional TEM image of a metal oxide film of oneembodiment of the present invention and FIGS. 1B to 1D are nanobeamelectron diffraction patterns thereof.

FIG. 2A is a plane TEM image of a metal oxide film of one embodiment ofthe present invention and FIG. 2B is a selected-area electrondiffraction pattern thereof.

FIGS. 3A to 3C are conceptual diagrams of electron diffraction intensitydistribution.

FIG. 4 is a nanobeam electron diffraction pattern of a quartz glasssubstrate.

FIGS. 5A and 5B are cross-sectional TEM images of a metal oxide film ofone embodiment of the present invention.

FIG. 6 shows a result of X-ray diffraction analysis of a metal oxidefilm of one embodiment of the present invention.

FIG. 7 is a nanobeam electron diffraction pattern of a metal oxide filmof one embodiment of the present invention.

FIG. 8 is a nanobeam electron diffraction pattern of a metal oxide filmof one embodiment of the present invention.

FIGS. 9A to 9C each illustrate a structural example of a transistor inone embodiment.

FIGS. 10A to 10D illustrate an example of a method for forming atransistor in one embodiment.

FIGS. 11A to 11C each illustrate a structural example of a transistor inone embodiment.

FIGS. 12A to 12C each illustrate a structure of a display panel in oneembodiment.

FIG. 13 is a block diagram of an electronic device in one embodiment.

FIGS. 14A to 14D are each an external view of an electronic device inone embodiment.

FIG. 15A is a cross-sectional TEM image of a metal oxide film of oneembodiment of the present invention and FIGS. 15B to 15E are nanobeamelectron diffraction patterns thereof.

FIG. 16 is a conceptual diagram illustrating a method for thinning asample by an ion milling method.

FIGS. 17A to 17D are each a nanobeam electron diffraction pattern of ametal oxide film of one embodiment of the present invention.

FIGS. 18A and 18B show SIMS analysis results of metal oxide films in acomparative example and one embodiment.

FIGS. 19A to 19D each show results of X-ray diffraction analysis ofsamples prepared by a liquid phase method.

FIGS. 20A to 20C are cross-sectional TEM images of a sample in acomparative example.

FIGS. 21A to 21C are nanobeam electron diffraction patterns of a samplein a comparative example and FIG. 21D is a nanobeam electron diffractionpattern of a metal oxide film of one embodiment of the presentinvention.

FIG. 22 illustrates a crystal structure of an oxide semiconductor layerused for calculation.

FIGS. 23A to 23D show calculation results for an influence of hydrogenaddition on a crystal state.

FIGS. 24A to 24D show measurement results of bond energy in a metaloxide film of one embodiment of the present invention and a sample in acomparative example by XPS.

BEST MODE FOR CARRYING OUT THE INVENTION

Hereinafter, embodiments of the present invention will be described indetail with reference to the accompanying drawings. Note that thepresent invention is not limited to the description below and it iseasily understood by those skilled in the art that the modes and theaspects can be changed in various ways. Therefore, the invention shouldnot be construed as being limited to the description in the followingembodiments.

Embodiment 1

In this embodiment, a metal oxide film of one embodiment of the presentinvention will be described with reference to FIGS. 1A to 1D, FIGS. 2Aand 2B, FIGS. 3A to 3C, FIG. 4, FIGS. 5A and 5B, FIG. 6, FIG. 7, FIGS.15A to 15E, FIG. 16, FIGS. 17A to 17D, FIGS. 18A and 18B, FIGS. 19A to19D, FIGS. 20A to 20C, and FIGS. 21A to 21D.

<Crystal Part in Metal Oxide Film>

The metal oxide film of this embodiment includes a minute crystal partin which periodic atomic arrangement is not observed macroscopically orlong-range order in atomic arrangement is not observed macroscopically.Therefore, spots having regularity that represents a crystal state arenot observed in some cases by electron diffraction when the measurementarea is larger (wider) than a crystal part included therein.

<<Cross-sectional TEM Image and Nanobeam Electron Diffraction Patterns>>

FIG. 1A is a cross-sectional transmission electron microscopy (TEM)image of the metal oxide film of this embodiment. FIGS. 1B, 1C, and 1Dare electron diffraction patterns observed by nanobeam electrondiffraction at points 1, 2, and 3 in FIG. 1A, respectively.

As an example of the metal oxide film, a 50-nm-thick In—Ga—Zn-basedoxide film was formed over a quartz glass substrate. The metal oxidefilm was formed under the following conditions: an oxide targetcontaining In, Ga, and Zn at an atomic ratio of 1:1:1 was used; anoxygen atmosphere (flow rate of 45 sccm) was used; the pressure was 0.4Pa; the direct current (DC) power supply was 0.5 kW; and the substratetemperature was room temperature. Then, the formed metal oxide film wasthinned to about 50 nm (e.g., 40 nm±10 nm) and a cross-sectional TEMimage and nanobeam electron diffraction patterns were observed.

The cross-sectional TEM image of the metal oxide film was observed witha transmission electron microscope (“H-9000NAR” manufactured by HitachiHigh-Technologies Corporation) at an acceleration voltage of 300 kV andat a magnification of 2000000 times. The nanobeam electron diffractionwas carried out with a transmission electron microscope (“HF-2000”manufactured by Hitachi High-Technologies Corporation) at anacceleration voltage of 200 kV and a beam diameter of about 1 nmφ. Notethat a measurement area of the nanobeam electron diffraction was greaterthan or equal to 5 nmφ and less than or equal to 10 nmφ.

As shown in FIG. 1B, in the nanobeam electron diffraction of the metaloxide film of this embodiment, circumferentially arranged spots (lightspots) were observed. This means that, in the case of the metal oxidefilm of this embodiment, a plurality of circumferentially distributedspots are observed. It can also be said that a plurality of concentriccircles are formed by a plurality of circumferentially distributedspots.

Further, also in FIG. 1C which shows the central portion of the metaloxide film in the thickness direction and in FIG. 1D which shows thevicinity of an interface with the quartz glass substrate, a plurality ofcircumferentially distributed spots are observed similarly to FIG. 1B.In FIG. 1C, the radius of a first circle (distance from a main spot tothe circumference) is in a range from 3.88/nm to 4.93/nm, or from 0.203nm to 0.257 nm when converted into interplanar spacing.

Apart from a halo pattern indicating an amorphous state, a plurality ofspots are observed in the nanobeam electron diffraction patterns shownin FIGS. 1B to 1D. This confirms that the metal oxide film of thisembodiment includes a crystal part. However, spots withoutdirectionality, which do not have regularity that represents crystalparts aligned with a specific plane, are observed in the nanobeamelectron diffraction patterns shown in FIGS. 1B to 1D. Accordingly, itis assumed that the metal oxide film of this embodiment includes aplurality of crystal parts whose surface orientations are random andwhose sizes are different from each other.

FIGS. 5A and 5B are partial enlarged views of the cross-sectional TEMimage of FIG. 1A. FIG. 5A is a cross-sectional TEM image of the vicinityof the point 1 (a surface of the metal oxide film) in FIG. 1A, which isobserved at an observation magnification of 8000000 times. FIG. 5B is across-sectional TEM image of the vicinity of the point 2 (the centralportion of the metal oxide film in the thickness direction) in FIG. 1A,which is observed at an observation magnification of 8000000 times.

In the cross-sectional TEM images of the metal oxide film of thisembodiment shown in FIGS. 5A and 5B, a crystal structure cannot beclearly observed.

<<Plane TEM Image and Selected-area Electron Diffraction Pattern>>

FIG. 2A is a plane TEM image of the metal oxide film of this embodiment.FIG. 2B shows an electron diffraction pattern of a region surrounded bya circle in FIG. 2A, which is observed by selected-area electrondiffraction.

As an example of the metal oxide film, a 50-nm-thick In—Ga—Zn-basedoxide film was formed over a quartz glass substrate. The metal oxidefilm was formed under the following conditions: an oxide targetcontaining In, Ga, and Zn at an atomic ratio of 1:1:1 was used; anoxygen atmosphere (flow rate of 45 sccm) was used; the pressure was 0.4Pa; the direct current (DC) power supply was 0.5 kW; and the substratetemperature was room temperature. Then, the formed metal oxide film wasthinned to about 50 nm (e.g., 40 nm±10 nm) and a plane TEM image and aselected-area electron diffraction pattern were observed.

The images in FIGS. 2A and 2B were obtained with a transmission electronmicroscope (“H-9000NAR” manufactured by Hitachi High-TechnologiesCorporation) at an acceleration voltage of 300 kV. To obtain the imagein FIG. 2A, a plane of the metal oxide film was observed at anobservation magnification of 500000 times. FIG. 2B shows a diffractionresult of the region in the circle in FIG. 2A obtained by selected-areaelectron diffraction. The pattern in FIG. 2B was obtained by electrondiffraction with a selected area of 300 nmφ. In consideration ofelectron beam expansion (about several nanometers), a measurement areais greater than or equal to 300 nmφ.

As shown in FIG. 2B, in the case of the metal oxide film of thisembodiment, the plurality of spots observed by nanobeam electrondiffraction were not observed and a halo pattern was observed in anelectron diffraction pattern observed by selected-area electrondiffraction the measurement area of which is wider than that of thenanobeam electron diffraction. Thus, the metal oxide film of thisembodiment can be regarded as a metal oxide film including a minutecrystal part in which periodic atomic arrangement is not observedmacroscopically (in the case where a measurement area is greater than orequal to 300 nmφ, for example) or long-range order in atomic arrangementis not observed macroscopically.

<<Conceptual Diagram of Electron Diffraction Intensity Distribution>>

FIGS. 3A to 3C conceptually illustrate diffraction intensitydistribution in the electron diffraction patterns in FIGS. 1B to 1D andFIGS. 2A and 2B. FIG. 3A is a conceptual diagram of diffractionintensity distribution in the nanobeam electron diffraction patterns inFIGS. 1B to 1D. FIG. 3B is a conceptual diagram of diffraction intensitydistribution in the selected-area electron diffraction pattern in FIG.2B. FIG. 3C is a conceptual diagram of diffraction intensitydistribution in an electron diffraction pattern of an idealpolycrystalline structure.

In each of FIGS. 3A to 3C, the vertical axis represents electrondiffraction intensity (arbitrary unit) and the horizontal axisrepresents a distance from a main spot.

In FIG. 3C for the ideal polycrystalline structure, a peak is observedat a specific distance from the main spot based on interplanar spacing(d value) of a plane with which crystal parts are aligned. In that case,in the electron diffraction pattern, a ring with a small line-width isclearly observed at the specific distance from the main spot.

On the other hand, as shown in FIGS. 1B to 1D, the circumferentialregion, which is formed with the plurality of spots observed in thenanobeam electron diffraction pattern of the metal oxide film of thisembodiment, has a relatively large line-width. Thus, its electron beamdiffraction intensity is discretely distributed and includes a pluralityof zones (peak zones) in which peaks are distributed, as shown in FIG.3A. Note that a small number of spots are observed between the pluralityof the circumferentially arranged regions in the nanobeam electrondiffraction pattern. This means that, as shown in FIG. 3A, diffractionpeaks exist between two peak zones.

On the other hand, the electron beam diffraction intensity distributionin the selected-area electron diffraction pattern of the metal oxidefilm of this embodiment is continuous as shown in FIG. 3B. Since FIG. 3Bcan approximate to a result obtained by observing the electron beamdiffraction intensity distribution shown in FIG. 3A in a wide area, itcan be considered that the peak zone in FIG. 3A is integrated and thecontinuous intensity distribution is obtained.

FIGS. 3A to 3C indicate that the metal oxide film of this embodimentincludes a plurality of crystal parts whose surface orientations arerandom and whose sizes are different from each other, and the crystalparts are so minute that spots are not observed in the selected-areaelectron diffraction patterns.

The metal oxide film which gives a plurality of spots in the nanobeamelectron diffraction pattern as shown in FIGS. 1B to 1D is thinned toabout 50 nm. Further, since the beam diameter of the electron beam isconverged to 1 nmφ, the measurement area is greater than or equal to 5nm and less than or equal to 10 nm. Accordingly, it is assumed that thesize of the crystal part included in the metal oxide film of thisembodiment is at least less than or equal to 50 nm, for example, lessthan or equal to 10 nm or less than or equal to 5 nm.

<<Nanobeam Electron Diffraction Pattern of Extremely Thin Sample>>

In the case where the size of the crystal part included in the metaloxide film of this embodiment is less than or equal to 10 nm or lessthan or equal to 5 nm, a measurement area in the depth direction islarger than the size of the crystal part in the sample in which themetal oxide film is thinned to about 50 nm; as a result, a plurality ofcrystal parts are observed in the measurement area, in some cases. Thus,a metal oxide film thinned to less than or equal to 10 nm was formed,and its cross section was observed by nanobeam electron diffraction.

A method for forming the sample is as follows. A 50-nm-thickIn—Ga—Zn-based oxide film was formed over a quartz glass substrate. Thefilm was formed under the following conditions: an oxide targetcontaining In, Ga, and Zn at an atomic ratio of 1:1:1 was used; anoxygen atmosphere (flow rate of 45 sccm) was used; the pressure was 0.4Pa; the direct current (DC) power supply was 0.5 kW; and the substratetemperature was room temperature. After the metal oxide film was formed,first heat treatment was performed at 450° C. in a nitrogen atmospherefor one hour and second heat treatment was performed at 450° C. in anatmosphere containing nitrogen and oxygen for one hour.

The metal oxide film on which the second heat treatment was performedwas further thinned by an ion milling method using Ar ions. First, thequartz glass substrate over which the metal oxide film was formed wasattached to a dummy substrate for reinforcement. Then, the film wasthinned to about 50 μm by cutting and polishing. After that, asillustrated in FIG. 16, a metal oxide film 204 provided to a quartzglass substrate 200 and a dummy substrate 202 were irradiated with argonions at a steep angle (about 3°) so that ion milling was performed toform a region 210 a which was thinned to about 50 nm (40 nm±10 nm) and aregion 210 b which was thinned to less than or equal to 10 nm, forexample, 5 nm to 10 nm. Then, the cross section of each region wasobserved.

FIG. 15A is a cross-sectional TEM image of a sample thinned to about 50nm, which corresponds to the region 210 a. FIGS. 15B to 15E showelectron diffraction patterns observed by nanobeam electron diffractionof the cross section shown in FIG. 15A. FIG. 15B shows an electrondiffraction pattern observed with the use of an electron beam whose beamdiameter is converged to 1 nmφ. FIG. 15C shows an electron diffractionpattern observed with the use of an electron beam whose beam diameter isconverged to 10 nmφ. FIG. 15D shows an electron diffraction patternobserved with the use of an electron beam whose beam diameter isconverged to 20 nmφ. FIG. 15E shows an electron diffraction patternobserved with the use of an electron beam whose beam diameter isconverged to 30 nmφ.

As shown in FIG. 15B, a plurality of circumferentially distributed spots(light spots), which are similar to those in FIGS. 1B to 1D, areobserved also in the metal oxide film on which heat treatment isperformed. Further, as shown in FIGS. 15C to 15E, when the beam diameterof an electron beam is increased to observe a wider measurement area,the spots are gradually blurred.

FIGS. 17A to 17D show nanobeam electron diffraction patterns at fourgiven points in a sample thinned to less than or equal to 10 nm, whichcorresponds to the region 210 b. The nanobeam electron diffractionpatterns are observed with the use of an electron beam whose beamdiameter is converged to 1 nmφ.

In FIGS. 17A and 17B, spots having regularity that represents crystalparts aligned with a specific plane are observed. This indicates thatthe metal oxide film of this embodiment undoubtedly includes a crystalpart. In FIGS. 17C and 17D, on the other hand, a plurality ofcircumferentially distributed spots (light spots) are observed.

As described above, the size of the crystal part included in the metaloxide film of this embodiment is minute and is at least less than orequal to 50 nm, for example, less than or equal to 10 nm or less than orequal to 5 nm. Thus, in the case where a sample is thinned to less thanor equal to 10 nm and the diameter of an electron beam is converged to 1nmφ to make a measurement area smaller than the size of one crystalpart, for example, spots having regularity that represents crystal partsaligned with a specific plane can be observed, depending the measuredregions. In the case where a plurality of crystal parts are included inthe observed region, an electron beam transmitted through a crystal partfurther irradiates another crystal part located in the depth direction,which would result in the observation of a plurality of nanobeamelectron diffraction patterns.

<<Nanobeam Electron Diffraction Pattern of Quartz Substrate>>

FIG. 4 shows a nanobeam electron diffraction pattern of a quartz glasssubstrate. The measurement conditions are the same as those for theoxide semiconductor film shown in FIGS. 1B to 1D.

As shown in FIG. 4, a halo pattern in which a specific spot is not givenby diffraction and whose luminance is gradually changed form a main spotis observed in the case of a quartz glass substrate having an amorphousstructure. Thus, circumferentially arranged spots like those observed inthe metal oxide film of this embodiment are not observed in a filmhaving an amorphous structure even when electron diffraction isperformed on a minute region. This confirms that the circumferentiallyarranged spots observed in FIGS. 1B to 1D are peculiar to the metaloxide film of this embodiment.

<<Electron Diffraction Pattern after Continuous Irradiation withNanobeam>>

FIG. 8 shows an electron diffraction pattern observed after the point 2in FIG. 1A is irradiated with an electron beam whose beam diameter isconverged to about 1 nmφ for one minute.

Similarly to the electron diffraction pattern shown in FIG. 1C, aplurality of circumferentially distributed spots are observed in theelectron diffraction pattern shown in FIG. 8, and there is nosignificant difference between the electron diffraction patterns in FIG.1C and FIG. 8. This means that the crystal part identified by FIG. 1C isformed when the metal oxide film of this embodiment is formed and is notresulted from the irradiation of the converged electron beam.

<<Analysis by X-Ray Diffraction>>

The sample of the metal oxide film of this embodiment formed over aquartz glass substrate, which is used for FIGS. 1A to 1D and FIGS. 2Aand 2B, was analyzed by X-ray diffraction (XRD). FIG. 6 shows an XRDspectrum measured by an out-of-plane method.

In FIG. 6, the vertical axis represents the X-ray diffraction intensity(arbitrary unit) and the horizontal axis represents the diffractionangle 2θ (degree). Note that the XRD spectra were measured with an X-raydiffractometer, D8 ADVANCE manufactured by Bruker AXS.

As shown in FIG. 6, a peak corresponding to quartz appears at around2θ=20° to 23°; however, a peak corresponding to the crystal partincluded in the metal oxide film cannot be found.

The result in FIG. 6 indicates that the crystal part included in themetal oxide film of this embodiment is minute.

According to the above results, it can be assumed that the metal oxidefilm of this embodiment is a film in which crystal parts whose surfaceorientations are random are cohered.

In addition, it is assumed that the size of a crystal part included inthe metal oxide film of this embodiment is less than or equal to 10 nmor less than or equal to 5 nm, for example. The metal oxide film of thisembodiment includes a crystal part (nanocrystal (nc)) whose size isgreater than or equal to 1 nm and less than or equal to 10 nm, forexample.

<Method for Forming Metal Oxide Film>

A method for forming the metal oxide film of this embodiment isdescribed below. As described above, the metal oxide film of thisembodiment is formed by a sputtering method at room temperature in anatmosphere containing oxygen. With the use of the atmosphere containingoxygen, oxygen vacancies in the metal oxide film can be reduced and afilm including a crystal part can be formed.

<<Reduction in Oxygen Vacancy>>

A reduction of oxygen vacancies in the metal oxide film of thisembodiment allows the formation of a film having stable physicalproperties. In particular, in the case where a semiconductor device isformed using an oxide semiconductor film as the metal oxide film of thisembodiment, oxygen vacancies in the oxide semiconductor film causecarriers to be generated; as a result, the electric characteristics ofthe semiconductor device vary. Thus, a semiconductor device formed usingan oxide semiconductor film in which oxygen vacancies are reduced can behighly reliable.

Note that it is preferable to increase the oxygen partial pressure inthe deposition atmosphere because the oxygen vacancies in the metaloxide film of this embodiment can be further reduced. For example, theoxygen partial pressure in the deposition atmosphere is preferablygreater than or equal to 33%.

FIG. 7 shows a nanobeam electron diffraction pattern of the metal oxidefilm of this embodiment which was formed at an oxygen partial pressureof 33%. The metal oxide film of this embodiment shown in FIG. 7 wasformed under conditions similar to those of the metal oxide film shownin FIGS. 1A to 1D except that a mixture of argon and oxygen (flow rateof Ar and O₂ are 30 sccm and 15 sccm, respectively) was used as thedeposition atmosphere. The nanobeam electron diffraction was carried outin a manner similar to that explained for FIGS. 1B to 1D.

In the metal oxide film of this embodiment which is formed at an oxygenpartial pressure of 33%, circumferentially arranged spots are alsoobserved in the nanobeam electron diffraction pattern shown in FIG. 7.This confirms that a metal oxide film including a crystal part isformed.

<<Deposition by Sputtering Method>>

An oxide target that can be used for forming the metal oxide film ofthis embodiment is not limited to an In—Ga—Zn-based oxide; for example,an In-M-Zn-based oxide (M is Al, Ti, Ga, Y, Zr, La, Ce, Nd, or Hf) canbe used.

The metal oxide film of this embodiment, which includes a crystal part,is preferably formed using a sputtering target including apolycrystalline oxide containing a plurality of crystal grains. Thereason is as follows. In the case where the sputtering target contains aplurality of crystal grains and there are interfaces that are likely tocause cleavage of the crystal grains because of weak bondings betweenthe plurality of crystal grains, the crystal grains are cleaved alongthe interfaces when ions collide with the sputtering target, wherebyflat plate-like sputtered particles can be obtained in some cases. Theobtained flat plate-like sputtered particles are deposited on asubstrate; accordingly, a metal oxide film including a nanocrystalregion is formed in some cases. Note that the above mechanism to formthe metal oxide film of this embodiment is one consideration.

The above-described metal oxide film of this embodiment includes aplurality of crystal parts whose surface orientations are random andwhose sizes are different from each other, and the crystal parts are sominute that spots are not observed in the selected-area electrondiffraction pattern.

Further, the metal oxide film of this embodiment includes a regionhaving a crystal part and has stable physical properties. Accordingly,with the use of the metal oxide film of this embodiment in asemiconductor device, the semiconductor device can have highreliability.

Comparative Example

In this comparative example, the crystallinity of a metal oxide filmformed by a liquid phase method will be described with reference todrawings.

A method for forming the metal oxide film of this comparative examplewill be described below.

First, In₂O₃ (5 wt %), Ga₂O₃ (3 wt %), ZnO (5 wt %), and a coating agentwere mixed so that the mixture contains In, Ga, and Zn at a compositionratio of 1:1:1, and the mixture was applied to a glass substrate by spincoating. The conditions for the spin coating were as follows: a spinnerwas used; and the spinning rate was changed stepwise from 900 rpm to2000 rpm.

After that, first heat treatment was performed at 150° C. in an airatmosphere for two minutes using a hot plate.

Subsequently, second heat treatment was performed at 450° C. in an airatmosphere for one hour. The bonding state of the metal oxide film(formed by a liquid phase method) of this comparative example subjectedto the second heat treatment, and the bonding state of the metal oxidefilm (formed by a sputtering method) of this embodiment formed under thesame conditions as those of the metal oxide film shown in FIG. 7 wereanalyzed by X-ray photoelectron spectroscopy (XPS). FIGS. 24A to 24Dshow the analysis results.

The XPS analysis was carried out with Quantera SXM manufactured byPhysical Electronics, Inc. as an analysis apparatus. FIGS. 24A to 24Dshow the spectra in the regions corresponding to 3d(5/2) orbital of In(see FIG. 24A), 3d orbital of Ga (see FIG. 24B), 3p orbital of Zn (seeFIG. 24C), and is orbital of O (see FIG. 24D) of each of the metal oxidefilms. Solid lines in FIGS. 24A to 24D corresponds to the analysisresults of the In—Ga—Zn oxide film of this comparative example, whichwas formed by a liquid phase method. Dashed lines in FIGS. 24A to 24Dcorresponds to the analysis results of the In—Ga—Zn oxide film of thisembodiment, which was formed by a sputtering method (sputtering).

In FIGS. 24A to 24D, although there is a slight difference between bondenergies, the metal oxide film of this comparative example, which wasformed by a liquid phase method, and the metal oxide film of thisembodiment, which was formed by a sputtering method, have substantiallythe same spectral shapes. Thus, the metal oxide film of this comparativeexample, which was formed by a liquid phase method, was identified as anIn—Ga—Zn oxide film.

Next, the formed samples of the comparative example were analyzed byXRD. FIGS. 19A to 19D show the results of the analysis by anout-of-plane method.

In the XRD analysis were used the samples of the In—Ga—Zn oxide filmwhich were subjected to the second heat treatment at 350° C., 450° C.,or 550° C. in an air atmosphere for one hour after the first heattreatment.

In FIGS. 19A to 19D, the vertical axis represents the X-ray diffractionintensity (arbitrary unit) and the horizontal axis represents thediffraction angle 2θ (degree). The XRD measurements were carried outwith an X-ray diffractometer, D8 ADVANCE manufactured by Bruker AXS.

FIG. 19A shows the measurement results of the samples of thiscomparative example formed by a liquid phase method. The XRD pattern ofthe sample which is not subjected to the heat treatment is the patterndenoted by “as-depo”. Note that FIGS. 19B to 19D show the measurementresults of indium oxide films, gallium oxide films, and zinc oxide filmswhich are formed by a liquid phase method and subjected to heattreatment at 350° C., 450° C., or 550° C. in an air atmosphere for onehour.

As shown in FIGS. 19A to 19D, peaks corresponding to In₂O₃ crystallinepeaks are found in the XRD pattern of the indium oxide films after theheat treatment. In addition, peaks corresponding to ZnO crystallinepeaks are found in the XRD pattern of the zinc oxide films after theheat treatment. In the samples of this comparative example subjected toheat treatment at any of the temperature, on the other hand, acrystalline peak is not found unlike in the indium oxide films and thezinc oxide films.

Then, the film density of each of the samples which were subjected tothe second heat treatment at 450° C. in an air atmosphere for one hourwas measured by X-ray reflectometry (XRR).

Note that XRR is a measurement method for measuring the density of adeposited thin film, in which X-rays are incident on a measurementsample to measure critical angles and changes in amplitude waveforms ofthe incident X-rays and theoretical analysis is performed using thecritical angles and the amplitude waveforms.

Table 1 shows the measured film density.

TABLE 1 Film Density (g/cm³) Sample Crystallinity Observed TheoreticalIn—Ga—Zn Oxide Film No peak 3.27 6.35 (In:Ga:Zn = 1:1:1) Indium OxideFilm Peak assignable to 4.26 7.12 In₂O₃ Gallium Oxide Film No peak 3.615.94 Zinc Oxide Film Peak assignable to 4.06 5.67 ZnO

As shown in Table 1, the films formed by a liquid phase method haveextremely low density as compared with the theoretical values calculatedon the basis of their single crystal structures. Note that it isdifficult to measure the film density with high accuracy because a filmformed by a liquid phase method has large roughness.

Next, the concentrations of impurities contained in the metal oxide filmof this comparative example and the metal oxide film of this embodimentwere measured by SIMS.

FIG. 18A shows concentration profiles of hydrogen (1H) in the metaloxide films of the comparative example and the metal oxide film of thisembodiment. FIG. 18B shows concentration profiles of carbon (12C) in themetal oxide films of the 20 comparative example and the metal oxide filmof this embodiment. In FIGS. 18A and 18B, the horizontal axis representsa depth (nm) and the vertical axis represents the concentration ofhydrogen or carbon (atoms/cm³).

Samples formed by a liquid phase method under the conditions similar tothose described above were used as the metal oxide films of thecomparative example for FIGS. 18A and 18B. Note that filtration using amembrane filter (0.2 μm) was performed on the material before spincoating. In addition, the second heat treatment was performed at 450°C., 500° C., or 550° C. in an air atmosphere for one hour. The otherconditions were the same as those of the above metal oxide films formedby a liquid phase method. A sample formed by a sputtering method underthe same conditions as those of the metal oxide film shown in FIG. 7 wasused for the metal oxide film of this embodiment.

As shown in FIGS. 18A and 18B, large amounts of hydrogen and carbonuniformly exist in the metal oxide films of the comparative example ascompared with the metal oxide film of this embodiment.

The carbon concentration of the metal oxide film of this embodimentshown in FIG. 18B is gradually decreased from its surface to the insidethe film. This suggests that carbon in the metal oxide film of thisembodiment is mainly due to the surface contamination.

In contrast, the metal oxide films formed under any conditions of thecomparative example uniformly contain hydrogen at a density as high as1×10²² (atoms/cm³) or more and carbon at a density as high as 4×10²¹(atoms/cm³) or more. It is assumed that carbon in the metal oxide filmsof the comparative example is due to an organic acid salt which is a rawmaterial of a spin coating material.

Next, cross-sectional TEM images of the sample of this comparativeexample, which was subjected to the second heat treatment at 450° C. inan air atmosphere for one hour, are shown in FIGS. 20A to 20C. The crosssection was observed with a transmission electron microscope(“H-9000NAR” manufactured by Hitachi High-Technologies Corporation) atan acceleration voltage of 300 kV. FIG. 20A is a cross-sectional imageat a magnification of 500000. FIG. 20B is a cross-sectional image at amagnification of 2000000. FIG. 20C is a cross-sectional observationimage at a magnification of 8000000.

As seen in FIGS. 20A and 20B, a large part of the sample of thiscomparative example formed by a liquid phase method is occupied by anamorphous region. In addition, a shade of gray (variation in brightness)due to the difference in film density can be seen.

In a region a in the cross-sectional TEM image in FIG. 20C, thebrightness is high, which means that the region a has low film density.In a region b in the cross-sectional TEM image in FIG. 20C, thebrightness is low, which means that the region b has high density.

The regions a and b in FIG. 20C were observed by nanobeam electrondiffraction. FIGS. 21A to 21C show nanobeam electron diffractionpatterns.

The nanobeam electron diffraction was carried out with a transmissionelectron microscope (“HF-2000” manufactured by Hitachi High-TechnologiesCorporation) at an acceleration voltage of 200 kV and a beam diameter ofabout 1 nmφ. FIG. 21A shows a nanobeam electron diffraction pattern ofthe region a in FIG. 20C. FIGS. 21B and 21C show nanobeam electrondiffraction patterns of two different portions (denoted by b1 and b2) inthe region b in FIG. 20C.

FIG. 21D shows a nanobeam electron diffraction pattern of the metaloxide film of one embodiment of the present invention, which was formedand observed under the same conditions as those of the metal oxide filmshown in FIG. 7.

As shown in FIGS. 21A to 21C, a pattern, which is different from thecircumferentially arranged spots (light spots) observed in the metaloxide film of one embodiment of the present invention shown in FIG. 21D,was observed in each region in the metal oxide film of this comparativeexample formed by a liquid phase method.

The nanobeam electron diffraction pattern of the region a shown in FIG.21A is similar to a halo pattern indicating an amorphous state. Thepresence of a region having such low crystallinity may be due to the lowdensity and the high impurity concentration of the film.

As shown in FIGS. 21B and 21C, spots (denoted by 1 to 3 in FIGS. 21B and21C) having regularity that represents crystal parts aligned with aspecific plane are observed in the nanobeam electron diffractionpatterns of the region b. The analysis results of the diffractionpatterns of these spots are shown in Table 2 below.

TABLE 2 d value (mm) Region Spot h k l Theoretical Observed b1 1 1 0 40.261 0.263 2 2 2 4 0.139 0.138 3 1 2 0 0.165 0.165 b2 1 0 0 9 0.2900.288 2 1 0 14 0.156 0.155 3 1 0 5 0.250 0.250

According to Table 2, the observed d values estimated from the spots inFIG. 21B or FIG. 21C are almost the same as the theoretical d values ofa plurality of plane orientations in InGaZnO₄, which means that theIn—Ga—Zn oxide film of this comparative example formed by a liquid phasemethod includes a crystal region due to InZnGaO₄.

Therefore, a region which includes periodic atomic arrangement due toInZnGaO₄ and a region which has extremely low crystallinity and is closeto an amorphous state coexist in the InZnGaO₄ film formed by a liquidphase method in spite of the presence of an impurity.

Next, the influence of impurities such as hydrogen and carbon in themetal oxide film of the comparative example on the crystallinity of themetal oxide film was evaluated by calculation.

In the calculation below, the effect of hydrogen on the crystallizationof the metal oxide film was examined by the first-principlescalculation. Specifically, an energy difference between an amorphousstate and a crystal state was measured in both the case where InGaZnO₄does not contain hydrogen and the case where the InGaZnO₄ containshydrogen at 6.67 atom %. An atom density of an In—Ga—Zn—O crystal of8.54×10²² atoms/cm³ and the SIMS analysis results shown in FIGS. 18A and18B indicate that this hydrogen concentration is the same as thehydrogen concentration of the metal oxide film of this comparativeexample. Note that an In—Ga—Zn oxide film containing In, Ga, and Zn atan atomic ratio of 1:1:1 was used as an example of the metal oxide filmfor the calculation.

FIG. 22 illustrates a lattice structure of an In—Ga—Zn—O crystalincluding 112 atoms used for the calculation.

For the calculation, a structure in which no H atom is added to thestructure illustrated in FIG. 22 and a structure in which eight H atomsare added to the structure illustrated in FIG. 22 were made, and thestructures were optimized. Then, energy was calculated. In addition,amorphous structures were formed on the basis of the optimized structurethrough the steps below.

(1) Molecular dynamics calculation with an NVT ensemble at 3000 K.(2) Molecular dynamics calculation with an NVT ensemble at 1000 K for 2psec.(3) Optimization of the structures.

Note that three structures were obtained by the above calculation (1)for 5 psec, 5.5 psec, or 6 psec, and then subjected to the calculation(2) and the optimization (3) to form three amorphous structures for eachof the three structures. Then, average values of energy were obtained.In the calculation, first principles calculation software “Vienna Abinitio Simulation Package (VASP)” was used. The calculation conditionsare shown in Table 3.

TABLE 3 Cutoff Energy Steps Functional (eV) K Points (1) GGA-PBE 500 1 ×1 × 1 (2) GGA-PBE 300 1 × 1 × 1 (3) GGA-PBE 500 2 × 2 × 3

FIGS. 23A to 23D illustrate part of each structures obtained by thecalculation. Table 4 shows the calculation results of the energydifference. FIG. 23A illustrates a structure in which no H atom (0 atom%) is added to a single crystal In—Ga—Zn oxide film. FIG. 23Billustrates a structure in which eight H atoms (6.67 atom %) are addedto a single crystal In—Ga—Zn oxide film. FIG. 23C illustrates astructure in which no H atom (0 atom %) is added to an amorphousIn—Ga—Zn oxide film FIG. 23D illustrates a structure in which eight Hatoms (6.67 atom %) are added to an amorphous In—Ga—Zn oxide film.

TABLE 4 Hydrogen concentration Density Energy difference (atom %)(g/cm³) (amorphous-single crystal) 0 6.12 1.23 6.67 5.82 0.54

According to Table 4, the energy of the In—Ga—Zn oxide film greatlydecreases when the film is crystallized. Further, the stabilizationenergy due to crystallization decreases when H atoms are added to thefilm. Accordingly, it is assumed that the observation of the nanobeamelectron diffraction pattern similar to a halo pattern in addition tothe spot-containing pattern indicating the periodic atomic arrangementin the metal oxide film of this comparative example formed by a liquidphase method is resulted from destabilization of the crystal structureby hydrogen.

As described above, when the metal oxide film contains hydrogen as animpurity, the stability of the crystal is decreased. These calculationresults agree with the high concentration of the impurity such ashydrogen and carbon in the metal oxide film of the comparative example,which shows a nanobeam electron diffraction pattern similar to a halopattern, when compared with the metal oxide film of this embodiment.

This embodiment can be implemented in combination with Embodimentdescribed in this specification as appropriate.

Embodiment 2

In this embodiment, a structural example of a transistor including themetal oxide film which is described as an example in Embodiment 1 andexhibits semiconductor characteristics (an oxide semiconductor film)will be described with reference to drawings.

<Structural Example of Transistor>

FIG. 9A is a schematic cross-sectional view of a transistor 100 which isdescribed below as an example. The transistor 100 is a bottom-gatetransistor.

The transistor 100 includes a gate electrode 102 provided over asubstrate 101, an insulating layer 103 provided over the substrate 101and the gate electrode 102, an oxide semiconductor layer 104 providedover the insulating layer 103 to overlap with the gate electrode 102,and a pair of electrodes 105 a and 105 b in contact with the top surfaceof the oxide semiconductor layer 104. Further, an insulating layer 106is provided to cover the insulating layer 103, the oxide semiconductorlayer 104, and the pair of electrodes 105 a and 105 b, and an insulatinglayer 107 is provided over the insulating layer 106.

The oxide semiconductor film of one embodiment of the present inventioncan be applied to the oxide semiconductor layer 104 in the transistor100.

<<Substrate 101>>

There is no particular limitation on the property of a material and thelike of the substrate 101 as long as the material has heat resistanceenough to withstand at least heat treatment which will be performedlater. For example, a glass substrate, a ceramic substrate, a quartzsubstrate, a sapphire substrate, or an yttria-stabilized zirconia (YSZ)substrate may be used as the substrate 101. Alternatively, a singlecrystal semiconductor substrate or a polycrystalline semiconductorsubstrate made of silicon, silicon carbide, or the like, a compoundsemiconductor substrate made of silicon germanium or the like, an SOIsubstrate, or the like can be used as the substrate 101. Stillalternatively, any of these substrates provided with a semiconductorelement may be used as the substrate 101.

Still alternatively, a flexible substrate such as a plastic substratemay be used as the substrate 101, and the transistor 100 may be provideddirectly on the flexible substrate. Further alternatively, a separationlayer may be provided between the substrate 101 and the transistor 100.The separation layer can be used when part or the whole of thetransistor formed over the separation layer is formed and separated fromthe substrate 101 and transferred to another substrate. Thus, thetransistor 100 can be transferred to a substrate having low heatresistance or a flexible substrate.

<<Gate Electrode 102>>

The gate electrode 102 can be formed using a metal selected fromaluminum, chromium, copper, tantalum, titanium, molybdenum, andtungsten; an alloy containing any of these metals as a component; analloy containing any of these metals in combination; or the like.Further, one or more metals selected from manganese and zirconium may beused. Furthermore, the gate electrode 102 may have a single-layerstructure or a stacked-layer structure of two or more layers. Forexample, a single-layer structure of an aluminum film containingsilicon, a two-layer structure in which a titanium film is stacked overan aluminum film, a two-layer structure in which a titanium film isstacked over a titanium nitride film, a two-layer structure in which atungsten film is stacked over a titanium nitride film, a two-layerstructure in which a tungsten film is stacked over a tantalum nitridefilm or a tungsten nitride film, a three-layer structure in which atitanium film, an aluminum film, and a titanium film are stacked in thisorder, and the like can be given. Alternatively, an alloy filmcontaining aluminum and one or more metals selected from titanium,tantalum, tungsten, molybdenum, chromium, neodymium, and scandium; or anitride film of the alloy film may be used.

The gate electrode 102 can also be formed using a light-transmittingconductive material such as indium tin oxide, indium oxide containingtungsten oxide, indium zinc oxide containing tungsten oxide, indiumoxide containing titanium oxide, indium tin oxide containing titaniumoxide, indium zinc oxide, or indium tin oxide to which silicon oxide isadded. It is also possible to have a stacked-layer structure formedusing the above light-transmitting conductive material and the abovemetal.

Further, an In—Ga—Zn-based oxynitride semiconductor film, an In—Sn-basedoxynitride semiconductor film, an In—Ga-based oxynitride semiconductorfilm, an In—Zn-based oxynitride semiconductor film, a Sn-basedoxynitride semiconductor film, an In-based oxynitride semiconductorfilm, a film of metal nitride (such as InN or ZnN), or the like may beprovided between the gate electrode 102 and the insulating layer 103.These films each have a work function higher than or equal to 5 eV orhigher than or equal to 5.5 eV, which is higher than the electronaffinity of the oxide semiconductor. Thus, the threshold voltage of thetransistor including an oxide semiconductor can be shifted in thepositive direction, and what is called a normally-off switching elementcan be achieved. For example, an In—Ga—Zn-based oxynitride semiconductorfilm having a higher nitrogen concentration than at least the oxidesemiconductor layer 104, specifically, an In—Ga—Zn-based oxynitridesemiconductor film having a nitrogen concentration of 7 atomic % orhigher is used.

<<Insulating Layer 103>>

The insulating layer 103 functions as a gate insulating film. Theinsulating layer 103 in contact with the bottom surface of the oxidesemiconductor layer 104 is preferably an amorphous film.

The insulating layer 103 may be formed to have a single-layer structureor a stacked-layer structure using, for example, one or more of siliconoxide, silicon oxynitride, silicon nitride oxide, silicon nitride,aluminum oxide, hafnium oxide, gallium oxide, Ga—Zn-based metal oxide,silicon nitride, and the like.

The insulating layer 103 may be formed using a high-k material such ashafnium silicate (HfSiO_(x)), hafnium silicate to which nitrogen isadded (HfSi_(x)O_(y)N_(z)), hafnium aluminate to which nitrogen is added(HfAl_(x)O_(y)N_(z)), hafnium oxide, or yttrium oxide, so that gateleakage current of the transistor can be reduced.

<<Pair of Electrodes 105 a and 105 b>>

The pair of electrodes 105 a and 105 b functions as a source electrodeand a drain electrode of the transistor.

The pair of electrodes 105 a and 105 b can be formed to have asingle-layer structure or a stacked-layer structure using, as aconductive material, any of metals such as aluminum, titanium, chromium,nickel, copper, yttrium, zirconium, molybdenum, silver, tantalum, andtungsten, or an alloy containing any of these metals. For example, asingle-layer structure of an aluminum film containing silicon, atwo-layer structure in which a titanium film is stacked over an aluminumfilm, a two-layer structure in which a titanium film is stacked over atungsten film, a two-layer structure in which a copper film is stackedover a copper-magnesium-aluminum alloy film, a three-layer structure inwhich a titanium film or a titanium nitride film, an aluminum film or acopper film, and a titanium film or a titanium nitride film are stackedin this order, a three-layer structure in which a molybdenum film or amolybdenum nitride film, an aluminum film or a copper film, and amolybdenum film or a molybdenum nitride film are stacked in this order,and the like can be given. Note that a transparent conductive materialcontaining indium oxide, tin oxide, or zinc oxide may be used.

<<Insulating Layer 106, 107>>

The insulating layer 106 is preferably formed using an oxide insulatingfilm containing oxygen at a higher proportion than oxygen in thestoichiometric composition. Such an oxide insulating film releasesoxygen upon heating. For instance, when such an oxide insulating film isheated at a temperature that is equal to or higher than a heat treatmenttemperature in a manufacturing process of a transistor, the amount ofreleased oxygen converted into oxygen atoms is greater than or equal to1.0×10¹⁸ atoms/cm³, preferably greater than or equal to 3.0×10²⁰atoms/cm³ in thermal desorption spectroscopy (TDS) analysis.

As the insulating layer 106, a silicon oxide film, a silicon oxynitridefilm, or the like can be formed.

Note that the insulating layer 106 also functions as a film whichrelieves damage to the oxide semiconductor layer 104 at the time offorming the insulating layer 107 later.

An oxide film transmitting oxygen may be provided between the insulatinglayer 106 and the oxide semiconductor layer 104.

As the oxide film transmitting oxygen, a silicon oxide film, a siliconoxynitride film, or the like can be formed. Note that in thisspecification, a “silicon oxynitride film” refers to a film thatcontains oxygen at a higher proportion than nitrogen, and a “siliconnitride oxide film” refers to a film that contains nitrogen at a higherproportion than oxygen.

The insulating layer 107 can be formed using an insulating film having ablocking effect against oxygen, hydrogen, water, and the like. It ispossible to prevent outward diffusion of oxygen from the oxidesemiconductor layer 104 and entry of hydrogen, water, or the like intothe oxide semiconductor layer 104 from the outside by providing theinsulating layer 107 over the insulating layer 106. As for such aninsulating film, a silicon nitride film, a silicon nitride oxide film,an aluminum oxide film, an aluminum oxynitride film, a gallium oxidefilm, a gallium oxynitride film, an yttrium oxide film, an yttriumoxynitride film, a hafnium oxide film, and a hafnium oxynitride film canbe given as examples.

<Example of Manufacturing Method of Transistor>

Next, an example of a fabrication method of the transistor 100illustrated in FIGS. 9A to 9C will be described.

First, as illustrated in FIG. 10A, the gate electrode 102 is formed overthe substrate 101, and the insulating layer 103 is formed over the gateelectrode 102.

Here, a glass substrate is used as the substrate 101.

<<Formation of Gate Electrode>>

A formation method of the gate electrode 102 is described below. First,a conductive film is formed by a sputtering method, a CVD method, anevaporation method, or the like and then a resist mask is formed overthe conductive film using a first photomask by a photolithographyprocess. Then, part of the conductive film is etched using the resistmask to form the gate electrode 102. After that, the resist mask isremoved.

Note that instead of the above formation method, the gate electrode 102may be formed by an electrolytic plating method, a printing method, anink-jet method, or the like.

<<Formation of Gate Insulating Layer>>

The insulating layer 103 is formed by a sputtering method, a CVD method,an evaporation method, or the like.

In the case where the insulating layer 103 is formed using a siliconoxide film, a silicon oxynitride film, or a silicon nitride oxide film,a deposition gas containing silicon and an oxidizing gas are preferablyused as a source gas. Typical examples of the deposition gas containingsilicon include silane, disilane, trisilane, and silane fluoride. As theoxidizing gas, oxygen, ozone, dinitrogen monoxide, and nitrogen dioxidecan be given as examples.

In the case of forming a silicon nitride film as the insulating layer103, it is preferable to use a two-step formation method. First, a firstsilicon nitride film with a small number of defects is formed by aplasma CVD method in which a mixed gas of silane, nitrogen, and ammoniais used as a source gas. Then, a second silicon nitride film in whichthe hydrogen concentration is low and hydrogen can be blocked is formedby switching the source gas to a mixed gas of silane and nitrogen. Withsuch a formation method, a silicon nitride film with a small number ofdefects and a blocking property against hydrogen can be formed as theinsulating layer 103.

Moreover, in the case of forming a gallium oxide film as the insulatinglayer 103, a metal organic chemical vapor deposition (MOCVD) method canbe employed.

<<Formation of Oxide Semiconductor Layer>>

Next, as illustrated in FIG. 10B, the oxide semiconductor layer 104 isformed over the insulating layer 103.

A formation method of the oxide semiconductor layer 104 is describedbelow. First, an oxide semiconductor film is formed using the methoddescribed in Embodiment 1. Then, a resist mask is formed over the oxidesemiconductor film using a second photomask by a photolithographyprocess. Then, part of the oxide semiconductor film is etched using theresist mask to form the oxide semiconductor layer 104. After that, theresist mask is removed.

After that, heat treatment may be performed. In such a case, the heattreatment is preferably performed under an atmosphere containing oxygen.

<<Formation of Pair of Electrodes>>

Next, as illustrated in FIG. 10C, the pair of electrodes 105 a and 105 bis formed.

A formation method of the pair of electrodes 105 a and 105 b isdescribed below. First, a conductive film is formed by a sputteringmethod, a CVD method, an evaporation method, or the like. Then, a resistmask is formed over the conductive film using a third photomask by aphotolithography process. Then, part of the conductive film is etchedusing the resist mask to form the pair of electrodes 105 a and 105 b.After that, the resist mask is removed.

Note that as illustrated in FIG. 10B, an upper part of the oxidesemiconductor layer 104 is in some cases partly etched and thinned bythe etching of the conductive film. For this reason, the oxidesemiconductor layer 104 is preferably formed thick.

<<Formation of Insulating Layer>>

Next, as illustrated in FIG. 10D, the insulating layer 106 is formedover the oxide semiconductor layer 104 and the pair of electrodes 105 aand 105 b, and the insulating layer 107 is successively formed over theinsulating layer 106.

In the case where the insulating layer 106 is formed using a siliconoxide film or a silicon oxynitride film, a deposition gas containingsilicon and an oxidizing gas are preferably used as a source gas.Typical examples of the deposition gas containing silicon includesilane, disilane, trisilane, and silane fluoride. As the oxidizing gas,oxygen, ozone, dinitrogen monoxide, and nitrogen dioxide can be given asexamples.

For example, a silicon oxide film or a silicon oxynitride film is formedunder the conditions as follows: the substrate placed in avacuum-evacuated treatment chamber of a plasma CVD apparatus is held ata temperature higher than or equal to 180° C. and lower than or equal to260° C., preferably higher than or equal to 200° C. and lower than orequal to 240° C., to the treatment chamber is charged a source gas at apressure greater than or equal to 100 Pa and less than or equal to 250Pa, preferably greater than or equal to 100 Pa and less than or equal to200 Pa, and high-frequency power higher than or equal to 0.17 W/cm² andlower than or equal to 0.5 W/cm², preferably higher than or equal to0.25 W/cm² and lower than or equal to 0.35 W/cm² is supplied to anelectrode provided in the treatment chamber.

With the application of the high-frequency power, the degradationefficiency of the source gas in plasma is increased, oxygen radicals areincreased, and oxidation of the source gas is promoted; therefore,oxygen is contained in the oxide insulating film at a higher proportionthan oxygen in the stoichiometric composition. However, the filmsprepared at the aforementioned substrate temperature release part ofoxygen therein upon heating performed in later processes. Thus, it ispossible to form an oxide insulating film which contains oxygen at ahigher proportion than oxygen in the stoichiometric composition and fromwhich part of oxygen is released by heating.

Further, in the case of providing an oxide insulating film between theoxide semiconductor layer 104 and the insulating layer 106, the oxideinsulating film serves as a protective film of the oxide semiconductorlayer 104 in the steps of forming the insulating layer 106. Thus, theinsulating layer 106 can be formed using the high-frequency power havinga high power density while damage to the oxide semiconductor layer 104is reduced.

For example, a silicon oxide film or a silicon oxynitride film can beformed as the oxide insulating film under the conditions as follows: thesubstrate placed in a vacuum-evacuated treatment chamber of a plasma CVDapparatus is held at a temperature higher than or equal to 180° C. andlower than or equal to 400° C., preferably higher than or equal to 200°C. and lower than or equal to 370° C., to the treatment chamber ischarged a source gas at a pressure greater than or equal to 20 Pa andless than or equal to 250 Pa, preferably greater than or equal to 100 Paand less than or equal to 250 Pa, and high-frequency power is suppliedto an electrode provided in the treatment chamber. Further, when thepressure in the treatment chamber is greater than or equal to 100 Pa andless than or equal to 250 Pa, damage to the oxide semiconductor layer104 can be reduced.

A deposition gas containing silicon and an oxidizing gas are preferablyused as a source gas of the oxide insulating film. Typical examples ofthe deposition gas containing silicon include silane, disilane,trisilane, and silane fluoride. As the oxidizing gas, oxygen, ozone,dinitrogen monoxide, and nitrogen dioxide can be given as examples.

The insulating layer 107 can be formed by a sputtering method, a CVDmethod, or the like.

In the case where the insulating layer 107 is formed using a siliconnitride film or a silicon nitride oxide film, a deposition gascontaining silicon, an oxidizing gas, and a gas containing nitrogen arepreferably used as a source gas. Typical examples of the deposition gascontaining silicon include silane, disilane, trisilane, and silanefluoride. As the oxidizing gas, oxygen, ozone, dinitrogen monoxide, andnitrogen dioxide can be given as examples. As the gas containingnitrogen, nitrogen and ammonia can be given as examples.

Through the above process, the transistor 100 can be formed.

<Modification Example of Transistor 100>

A structural example of a transistor, which is partly different from thetransistor 100, will be described below.

Modification Example 1

FIG. 9B is a schematic cross-sectional view of a transistor 110described as an example below. The transistor 110 is different from thetransistor 100 in the structure of an oxide semiconductor layer. Notethat descriptions of components having structures or functions similarto those of the other structural examples, which are denoted by the samereference numerals, are omitted below.

In an oxide semiconductor layer 114 included in the transistor 110, anoxide semiconductor layer 114 a and an oxide semiconductor layer 114 bare stacked.

Since a boundary between the oxide semiconductor layer 114 a and theoxide semiconductor layer 114 b is unclear in some cases, the boundaryis shown by a dashed line in FIG. 9B and the like.

The oxide semiconductor film of one embodiment of the present inventioncan be applied to one or both of the oxide semiconductor layers 114 aand 114 b.

Typical examples of a material that can be used for the oxidesemiconductor layer 114 a are an In—Ga oxide, an In—Zn oxide, and anIn-M-Zn oxide (M is Al, Ti, Ga, Y, Zr, La, Ce, Nd, or Hf). In the caseof using an In-M-Zn oxide for the oxide semiconductor layer 114 a, whensummation of In and M is assumed to be 100 atomic % and Zn and oxygenare eliminated from consideration, the proportions of In and M arepreferably greater than or equal to 25 atomic % and less than 75 atomic%, respectively, and further preferably greater than or equal to 34atomic % and less than 66 atomic %, respectively. Further, a materialhaving an energy gap of 2 eV or more, preferably 2.5 eV or more, furtherpreferably 3 eV or more is used for the oxide semiconductor layer 114 a,for example.

For example, the oxide semiconductor layer 114 b contains In or Ga andtypically contains an In—Ga oxide, an In—Zn oxide, or In-M-Zn oxide (Mis Al, Ti, Ga, Y, Zr, La, Ce, Nd, or Hf). In addition, energy level ofthe conduction band minimum of the oxide semiconductor layer 114 b iscloser to the vacuum level than that of the oxide semiconductor layer114 a is. The difference between energy level of the conduction bandminimum of the oxide semiconductor layer 114 b and energy level of theconduction band minimum of the oxide semiconductor layer 114 a ispreferably 0.05 eV or more, 0.07 eV or more, 0.1 eV or more, or 0.15 eVor more and 2 eV or less, 1 eV or less, 0.5 eV or less, or 0.4 eV orless.

When an In-M-Zn oxide is used as the oxide semiconductor layer 114 b,for example, the atomic ratio between In and M is preferably as follows:the atomic percentage of In is less than 50 atomic % and the atomicpercentage of M is greater than or equal to 50 atomic %; furtherpreferably, the atomic percentage of In is less than 25 atomic % and theatomic percentage of M is greater than or equal to 75 atomic %, wheresummation of In and M is assumed to be 100 atomic % and Zn and oxygenare eliminated from consideration.

For the oxide semiconductor layer 114 a, an In—Ga—Zn oxide containingIn, Ga, and Zn at an atomic ratio of 1:1:1 or 3:1:2 can be used, forexample. Further, for the oxide semiconductor layer 114 b, an In—Ga—Znoxide containing In, Ga, and Zn at an atomic ratio of 1:3:2, 1:6:4, or1:9:6 can be used. Note that the atomic ratios of the oxidesemiconductor layers 114 a and 114 b can be different from those of theused targets in some cases and there could be a difference of ±20%therebetween.

When an oxide containing a large amount of Ga that serves as astabilizer is used for the oxide semiconductor layer 114 b provided overthe oxide semiconductor layer 114 a, oxygen can be prevented from beingreleased from the oxide semiconductor layers 114 a and 114 b.

Note that, without limitation to the compositions and materialsdescribed above, a material with an appropriate composition may be useddepending on required semiconductor characteristics and electricalcharacteristics (e.g., field-effect mobility and threshold voltage) of atransistor. Further, in order to obtain required semiconductorcharacteristics of a transistor, it is preferable that the carrierdensity, the impurity concentration, the defect density, the atomicratio of a metal element to oxygen, the interatomic distance, thedensity, and the like of the oxide semiconductor layers 114 a and 114 bbe set to be appropriate.

Although a structure in which two oxide semiconductor layers are stackedis described above as an example of the oxide semiconductor layer 114, astructure in which three or more oxide semiconductor layers are stackedcan also be employed.

Modification Example 2

FIG. 9C is a schematic cross-sectional view of a transistor 120described as an example below. The transistor 120 is different in thestructure of an oxide semiconductor layer from the transistor 100 andthe transistor 110.

In an oxide semiconductor layer 124 included in the transistor 120, anoxide semiconductor layer 124 a, an oxide semiconductor layer 124 b, andan oxide semiconductor layer 124 c are stacked in this order.

The oxide semiconductor layers 124 a and 124 b are stacked over theinsulating layer 103. The oxide semiconductor layer 124 c is provided incontact with the top surface of the oxide semiconductor layer 124 b andthe top surfaces and side surfaces of the pair of electrodes 105 a and105 b.

The oxide semiconductor film of one embodiment of the present inventioncan be applied to at least one of the oxide semiconductor layers 124 a,124 b, and 124 c.

The oxide semiconductor layer 124 b can have a structure which issimilar to that of the oxide semiconductor layer 114 a described as anexample in Modification Example 1, for example. Further, the oxidesemiconductor layers 124 a and 124 c can each have a structure which issimilar to that of the oxide semiconductor layer 114 b described as anexample in Modification Example 1, for example

When an oxide containing a large amount of Ga that serves as astabilizer is used for the oxide semiconductor layer 124 a and the oxidesemiconductor layer 124 c, for example, oxygen can be prevented frombeing released from the oxide semiconductor layer 124 a, the oxidesemiconductor layer 124 b, and the oxide semiconductor layer 124 c.

In the case where a channel is mainly formed in the oxide semiconductorlayer 124 b, for example, an oxide containing a large amount of In canbe used for the oxide semiconductor layer 124 b and the pair ofelectrodes 105 a and 105 b is provided in contact with the oxidesemiconductor layer 124 b; thus, the on-state current of the transistor120 can be increased.

<Another Structure Example of Transistor>

A structure example of a top-gate transistor to which the oxidesemiconductor film of one embodiment of the present invention can beapplied will be described below.

<<Structural Example>>

FIG. 11A is a schematic cross-sectional view of a top-gate transistor150 which will be described below as an example.

The transistor 150 includes the oxide semiconductor layer 104 providedover the substrate 101 on which an insulating layer 151 is provided, thepair of electrodes 105 a and 105 b in contact with the top surface ofthe oxide semiconductor layer 104, the insulating layer 103 providedover the oxide semiconductor layer 104 and the pair of electrodes 105 aand 105 b, and the gate electrode 102 provided over the insulating layer103 to overlap with the oxide semiconductor layer 104. Further, aninsulating layer 152 is provided to cover the insulating layer 103 andthe gate electrode 102.

The oxide semiconductor film of one embodiment of the present inventioncan be applied to the oxide semiconductor layer 104 in the transistor150.

The insulating layer 151 has a function of suppressing diffusion ofimpurities from the substrate 101 to the oxide semiconductor layer 104.For example, a structure similar to that of the insulating layer 107 canbe employed. Note that the insulating layer 151 is not necessarilyprovided.

The insulating layer 152 can be formed using an insulating film having ablocking effect against oxygen, hydrogen, water, and the like in amanner similar to that of the insulating layer 107. Note that theinsulating layer 107 is not necessarily provided.

Modification Example

A structural example of a transistor, which is partly different from thetransistor 150, will be described below.

FIG. 11B is a schematic cross-sectional view of a transistor 160described as an example below. The structure of an oxide semiconductorlayer in the transistor 160 is different from that in the transistor150.

In an oxide semiconductor layer 164 included in the transistor 160, anoxide semiconductor layer 164 a, an oxide semiconductor layer 164 b, andan oxide semiconductor layer 164 c are stacked in this order.

The oxide semiconductor film of one embodiment of the present inventioncan be applied to at least one of the oxide semiconductor layer 164 a,the oxide semiconductor layer 164 b, and the oxide semiconductor layer164 c.

The oxide semiconductor layer 164 b can have a structure which issimilar to that of the oxide semiconductor layer 114 a described as anexample in Modification Example 1, for example. Further, the oxidesemiconductor layers 164 a and 164 c can each have a structure which issimilar to that of the oxide semiconductor layer 114 b described as anexample in Modification Example 1, for example.

An oxide containing a large amount of Ga that serves as a stabilizer isused for the oxide semiconductor layer 164 a and the oxide semiconductorlayer 164 c; thus, oxygen can be prevented from being released from theoxide semiconductor layer 164 a, the oxide semiconductor layer 164 b,and the oxide semiconductor layer 164 c.

The oxide semiconductor layer 164 can be formed in the following manner:the oxide semiconductor layer 164 c and the oxide semiconductor layer164 b are obtained by etching, so that an oxide semiconductor film to bethe oxide semiconductor layer 164 a is exposed; and the oxidesemiconductor film is processed into the oxide semiconductor layer 164 aby a dry etching method. In that case, a reaction product of the oxidesemiconductor film is attached to side surfaces of the oxidesemiconductor layers 164 b and 164 c to form a sidewall protective layer(also referred to as a rabbit ear) in some cases. Note that the reactionproduct is attached by a sputtering phenomenon or at the time of the dryetching.

FIG. 11C is a schematic cross-sectional view of a transistor 161 inwhich a sidewall protective layer 164 d is formed as a side surface ofthe oxide semiconductor layer 164 in the above manner. Note that theother components of the transistor 161 are the same as those of thetransistor 160.

The sidewall protective layer 164 d mainly contains the same material asthe oxide semiconductor layer 164 a. In some cases, the sidewallprotective layer 164 d contains the constituent (e.g., silicon) of alayer provided below the oxide semiconductor layer 164 a (the insulatinglayer 151 here).

With a structure in which a side surface of the oxide semiconductorlayer 164 b is covered with the sidewall protective layer 164 d so asnot to be in contact with the pair of electrodes 105 a and 105 b asillustrated in FIG. 11C, unintended leakage current of the transistor inan off state can be reduced particularly when a channel is mainly formedin the oxide semiconductor layer 164 b; thus, a transistor havingfavorable off-state characteristics can be fabricated. Further, when amaterial containing a large amount of Ga that serves as a stabilizer isused for the sidewall protective layer 164 d, oxygen can be effectivelyprevented from being released from the side surface of the oxidesemiconductor layer 164 b; thus, a transistor having excellent stabilityof electric characteristics can be fabricated.

This embodiment can be implemented in combination with Embodimentdescribed in this specification as appropriate.

Embodiment 3

In this embodiment, a structure of a display panel of one embodiment ofthe present invention will be described with reference to FIGS. 12A to12C.

FIG. 12A is a top view of the display panel of one embodiment of thepresent invention. FIG. 12B illustrates a pixel circuit that can be usedin the case where a liquid crystal element is used in a pixel in thedisplay panel of one embodiment of the present invention. FIG. 12Cillustrates a pixel circuit that can be used in the case where anorganic EL element is used in a pixel in the display panel of oneembodiment of the present invention.

The transistor in the pixel portion can be formed in accordance withEmbodiment 2. Further, the transistor can be easily formed as ann-channel transistor, and thus part of a driver circuit that can beformed using an n-channel transistor can be formed over the samesubstrate as the transistor of the pixel portion. With the use of thetransistor described in Embodiment 2 for the pixel portion or the drivercircuit in this manner, a highly reliable display device can beprovided.

FIG. 12A illustrates an example of a block diagram of an active matrixdisplay device. A pixel portion 501, a first scan line driver circuit502, a second scan line driver circuit 503, and a signal line drivercircuit 504 are provided over a substrate 500 in the display device. Inthe pixel portion 501, a plurality of signal lines extended from thesignal line driver circuit 504 are arranged and a plurality of scanlines extended from the first scan line driver circuit 502 and thesecond scan line driver circuit 503 are arranged. Note that pixels whichinclude display elements are provided in a matrix in respective regionswhere the scan lines and the signal lines intersect with each other. Thesubstrate 500 of the display device is connected to a timing controlcircuit (also referred to as a controller or a controller IC) through aconnection portion such as a flexible printed circuit (FPC).

In FIG. 12A, the first scan line driver circuit 502, the second scanline driver circuit 503, and the signal line driver circuit 504 areformed over the same substrate 500 as the pixel portion 501.Accordingly, the number of components which are provided outside, suchas a drive circuit, can be reduced, so that a reduction in cost can beachieved. Further, in the case where the driver circuit is providedoutside the substrate 500, wirings would need to be extended and thenumber of connections of wirings would be increased, but when the drivercircuit is provided over the substrate 500, the number of connections ofthe wirings can be reduced. Consequently, an improvement in reliabilityor yield can be achieved.

<Liquid Crystal Panel>

FIG. 12B illustrates an example of a circuit configuration of the pixel.Here, a pixel circuit which is applicable to a pixel of a VA liquidcrystal display panel is illustrated.

This pixel circuit can be applied to a structure in which one pixelincludes a plurality of pixel electrode layers. The pixel electrodelayers are connected to different transistors, and the transistors canbe driven with different gate signals. Accordingly, signals applied toindividual pixel electrode layers in a multi-domain pixel can becontrolled independently.

A gate wiring 512 of a transistor 516 and a gate wiring 513 of atransistor 517 are separated so that different gate signals can besupplied thereto. In contrast, a source or drain electrode 514functioning as a data line is shared by the transistors 516 and 517. Thetransistor described in Embodiment 2 can be used as appropriate as eachof the transistors 516 and 517. Thus, a highly reliable liquid crystaldisplay panel can be provided.

The shapes of a first pixel electrode layer electrically connected tothe transistor 516 and a second pixel electrode layer electricallyconnected to the transistor 517 are described. The first pixel electrodelayer and the second pixel electrode layer are separated by a slit. Thefirst pixel electrode layer has a V shape and the second pixel electrodelayer is provided so as to surround the first pixel electrode layer.

A gate electrode of the transistor 516 is connected to the gate wiring512, and a gate electrode of the transistor 517 is connected to the gatewiring 513. When different gate signals are supplied to the gate wiring512 and the gate wiring 513, operation timings of the transistor 516 andthe transistor 517 can be varied. As a result, alignment of liquidcrystals can be controlled.

Further, a storage capacitor may be formed using a capacitor wiring 510,a gate insulating film functioning as a dielectric, and a capacitorelectrode electrically connected to the first pixel electrode layer orthe second pixel electrode layer.

The multi-domain pixel includes a first liquid crystal element 518 and asecond liquid crystal element 519. The first liquid crystal element 518includes the first pixel electrode layer, a counter electrode layer, anda liquid crystal layer therebetween. The second liquid crystal element519 includes the second pixel electrode layer, a counter electrodelayer, and a liquid crystal layer therebetween.

Note that a pixel circuit of the present invention is not limited tothat shown in FIG. 12B. For example, a switch, a resistor, a capacitor,a transistor, a sensor, a logic circuit, or the like may be added to thepixel illustrated in FIG. 12B.

<Organic EL Panel>

FIG. 12C illustrates another example of a circuit configuration of thepixel portion. Here, a pixel structure of a display panel using anorganic EL element is shown.

In an organic EL element, by application of voltage to a light-emittingelement, electrons are injected from one of a pair of electrodes andholes are injected from the other of the pair of electrodes, into alayer containing a light-emitting organic compound; thus, current flows.The electrons and holes are recombined, and thus, the light-emittingorganic compound is excited. The light-emitting organic compound returnsto a ground state from the excited state, thereby emitting light. Owingto such a mechanism, this light-emitting element is referred to as acurrent-excitation light-emitting element.

FIG. 12C illustrates an applicable example of a pixel circuit. Here, onepixel includes two n-channel transistors. Note that the metal oxide filmof one embodiment of the present invention can be used for channelformation regions of the n-channel transistors. Further, digital timegrayscale driving can be employed for the pixel circuit.

The configuration of the applicable pixel circuit and operation of apixel employing digital time grayscale driving will be described.

A pixel 520 includes a switching transistor 521, a driver transistor522, a light-emitting element 524, and a capacitor 523. A gate electrodelayer of the switching transistor 521 is connected to a scan line 526, afirst electrode (one of a source electrode layer and a drain electrodelayer) of the switching transistor 521 is connected to a signal line525, and a second electrode (the other of the source electrode layer andthe drain electrode layer) of the switching transistor 521 is connectedto a gate electrode layer of the driver transistor 522. The gateelectrode layer of the driver transistor 522 is connected to a powersupply line 527 through the capacitor 523, a first electrode of thedriver transistor 522 is connected to the power supply line 527, and asecond electrode of the driver transistor 522 is connected to a firstelectrode (a pixel electrode) of the light-emitting element 524. Asecond electrode of the light-emitting element 524 corresponds to acommon electrode 528. The common electrode 528 is electrically connectedto a common potential line provided over the same substrate.

As the switching transistor 521 and the driver transistor 522, thetransistor described in Embodiment 2 can be used as appropriate. In thismanner, a highly reliable organic EL display panel can be provided.

The potential of the second electrode (the common electrode 528) of thelight-emitting element 524 is set to be a low power supply potential.Note that the low power supply potential is lower than a high powersupply potential supplied to the power supply line 527. For example, thelow power supply potential can be GND, 0V, or the like. The high powersupply potential and the low power supply potential are set to be higherthan or equal to the forward threshold voltage of the light-emittingelement 524, and the difference between the potentials is applied to thelight-emitting element 524, whereby current is supplied to thelight-emitting element 524, leading to light emission. The forwardvoltage of the light-emitting element 524 refers to a voltage at which adesired luminance is obtained, and is at least higher than a forwardthreshold voltage.

Note that gate capacitance of the driver transistor 522 may be used as asubstitute for the capacitor 523, so that the capacitor 523 can beomitted. The gate capacitance of the driver transistor 522 may be formedbetween the channel formation region and the gate electrode layer.

Next, a signal input to the driver transistor 522 is described. In thecase of a voltage-input voltage driving method, a video signal forturning on or off the driver transistor 522 without fail is input to thedriver transistor 522. In order for the driver transistor 522 to operatein a linear region, voltage higher than the voltage of the power supplyline 527 is applied to the gate electrode layer of the driver transistor522. Note that voltage higher than or equal to voltage which is the sumof power supply line voltage and the threshold voltage Vth of the drivertransistor 522 is applied to the signal line 525.

In the case of performing analog grayscale driving, a voltage greaterthan or equal to a voltage which is the sum of the forward voltage ofthe light-emitting element 524 and the threshold voltage Vth of thedriver transistor 522 is applied to the gate electrode layer of thedriver transistor 522. A video signal by which the driver transistor 522is operated in a saturation region is input, so that current is suppliedto the light-emitting element 524. In order for the driver transistor522 to operate in a saturation region, the potential of the power supplyline 527 is set higher than the gate potential of the driver transistor522. When an analog video signal is used, it is possible to supplycurrent to the light-emitting element 524 in accordance with the videosignal and perform analog grayscale driving.

Note that the configuration of the pixel circuit of the presentinvention is not limited to that shown in FIG. 12C. For example, aswitch, a resistor, a capacitor, a sensor, a transistor, a logiccircuit, or the like may be added to the pixel circuit illustrated inFIG. 12C.

Embodiment 4

In this embodiment, structures of a semiconductor device including themetal oxide film of one embodiment of the present invention andelectronic devices will be described with reference to FIG. 13 and FIGS.14A to 14D.

FIG. 13 is a block diagram of an electronic device including thesemiconductor device to which the metal oxide film of one embodiment ofthe present invention is applied.

FIGS. 14A to 14D are external views of electronic devices each includingthe semiconductor device to which the metal oxide film of one embodimentof the present invention is applied.

An electronic device illustrated in FIG. 13 includes an RF circuit 901,an analog baseband circuit 902, a digital baseband circuit 903, abattery 904, a power supply circuit 905, an application processor 906, aflash memory 910, a display controller 911, a memory circuit 912, adisplay 913, a touch sensor 919, an audio circuit 917, a keyboard 918,and the like.

The application processor 906 includes a CPU 907, a DSP 908, and aninterface (IF) 909. Moreover, the memory circuit 912 can include an SRAMor a DRAM.

The transistor described in Embodiment 2 is applied to the memorycircuit 912, whereby a highly reliable electronic device which can writeand read data can be provided.

The transistor described in Embodiment 2 is applied to a register or thelike included in the CPU 907 or the DSP 908, whereby a highly reliableelectronic device which can write and read data can be provided.

Note that in the case where the off-state leakage current of thetransistor described in Embodiment 2 is extremely small, the memorycircuit 912 can store data for a long time and can have sufficientlyreduced power consumption. Moreover, the CPU 907 or the DSP 908 canstore the state before power gating in a register or the like during aperiod in which the power gating is performed.

Further, the display 913 includes a display portion 914, a source driver915, and a gate driver 916.

The display portion 914 includes a plurality of pixels arranged in amatrix. The pixel includes a pixel circuit, and the pixel circuit iselectrically connected to the gate driver 916.

The transistor described in Embodiment 2 can be used as appropriate inthe pixel circuit or the gate driver 916. Accordingly, a highly reliabledisplay can be provided.

Examples of electronic devices are a television set (also referred to asa television or a television receiver), a monitor of a computer or thelike, a camera such as a digital camera or a digital video camera, adigital photo frame, a mobile phone handset (also referred to as amobile phone or a mobile phone device), a portable game machine, aportable information terminal, an audio reproducing device, alarge-sized game machine such as a pachinko machine, and the like.

FIG. 14A illustrates a portable information terminal, which includes amain body 1001, a housing 1002, a display portion 1003 a, a displayportion 1003 b, and the like. The display portion 1003 b includes atouch panel. By touching a keyboard button 1004 displayed on the displayportion 1003 b, screen operation can be carried out, and text can beinput. Needless to say, the display portion 1003 a may functions as atouch panel. A liquid crystal panel or an organic light-emitting panelis fabricated by using the transistor described in Embodiment 2 as aswitching element and applied to the display portion 1003 a or 1003 b,whereby a highly reliable portable information terminal can be provided.

The portable information terminal illustrated in FIG. 14A can have afunction of displaying a variety of kinds of data (e.g., a still image,a moving image, and a text image), a function of displaying a calendar,a date, the time, or the like on the display portion, a function ofoperating or editing data displayed on the display portion, a functionof controlling processing by a variety of kinds of software (programs),and the like. Further, an external connection terminal (an earphoneterminal, a USB terminal, or the like), a recording medium insertionportion, or the like may be provided on the back surface or the sidesurface of the housing.

The portable information terminal illustrated in FIG. 14A may transmitand receive data wirelessly. Through wireless communication, desiredbook data or the like can be purchased and downloaded from an electronicbook server.

FIG. 14B illustrates a portable music player including, in a main body1021, a display portion 1023, a fixing portion 1022 with which theportable music player can be worn on the ear, a speaker, an operationbutton 1024, an external memory slot 1025, and the like. A liquidcrystal panel or an organic light-emitting panel is fabricated by usingthe transistor described in Embodiment 2 as a switching element andapplied to the display portion 1023, whereby a highly reliable portablemusic player can be provided.

Furthermore, when the portable music player illustrated in FIG. 14B hasan antenna, a microphone function, or a wireless communication functionand is used with a mobile phone, a user can talk on the phone wirelesslyin a hands-free way while driving a car or the like.

FIG. 14C illustrates a mobile phone which includes two housings, ahousing 1030 and a housing 1031. The housing 1031 includes a displaypanel 1032, a speaker 1033, a microphone 1034, a pointing device 1036, acamera lens 1037, an external connection terminal 1038, and the like.The housing 1030 is provided with a solar cell 1040 for charging themobile phone, an external memory slot 1041, and the like. In addition,an antenna is incorporated in the housing 1031. The transistor describedin Embodiment 2 is applied to the display panel 1032, whereby a highlyreliable mobile phone can be provided.

Further, the display panel 1032 includes a touch panel. A plurality ofoperation keys 1035 which are displayed as images are indicated bydotted lines in FIG. 14C. Note that a boosting circuit by which avoltage output from the solar cell 1040 is increased so as to besufficiently high for each circuit is also included.

For example, a power transistor used for a power supply circuit such asa boosting circuit can also be formed when the metal oxide film of thetransistor described in the Embodiment 2 has a thickness greater than orequal to 2 μm and less than or equal to 50 μm.

In the display panel 1032, the direction of display is changed asappropriate depending on the application mode. Further, the mobile phoneis provided with the camera lens 1037 on the same surface as the displaypanel 1032, and thus it can be used as a video phone. The speaker 1033and the microphone 1034 can be used for videophone calls, recording, andplaying sound, and the like as well as voice calls. Moreover, thehousings 1030 and 1031 in a state where they are developed asillustrated in FIG. 14C can shift, by sliding, to a state where one islapped over the other. Therefore, the size of the mobile phone can bereduced, which makes the mobile phone suitable for being carried around.

The external connection terminal 1038 can be connected to an AC adaptorand a variety of cables such as a USB cable, whereby charging and datacommunication with a personal computer or the like are possible.Further, by inserting a recording medium into the external memory slot1041, a larger amount of data can be stored and moved.

Further, in addition to the above functions, an infrared communicationfunction, a television reception function, or the like may be provided.

FIG. 14D illustrates an example of a television set. In a television set1050, a display portion 1053 is incorporated in a housing 1051. Imagescan be displayed on the display portion 1053. Moreover, a CPU isincorporated in a stand 1055 for supporting the housing 1051. Thetransistor described in Embodiment 2 is applied to the display portion1053 and the CPU, whereby the television set 1050 can be highlyreliable.

The television set 1050 can be operated with an operation switch of thehousing 1051 or a separate remote controller. Further, the remotecontroller may be provided with a display portion for displaying dataoutput from the remote controller.

Note that the television set 1050 is provided with a receiver, a modem,and the like. With the use of the receiver, the television set 1050 canreceive general TV broadcasts. Moreover, when the television set 1050 isconnected to a communication network with or without wires via themodem, one-way (from a sender to a receiver) or two-way (between asender and a receiver or between receivers) information communicationcan be performed.

Further, the television set 1050 is provided with an external connectionterminal 1054, a storage medium recording and reproducing portion 1052,and an external memory slot. The external connection terminal 1054 canbe connected to various types of cables such as a USB cable, wherebydata communication with a personal computer or the like is possible. Adisk storage medium is inserted into the storage medium recording andreproducing portion 1052, and reading data stored in the storage mediumand writing data to the storage medium can be performed. In addition, animage, a video, or the like stored as data in an external memory 1056inserted into the external memory slot can be displayed on the displayportion 1053.

Further, in the case where the off-state leakage current of thetransistor described in Embodiment 2 is extremely small, when thetransistor is applied to the external memory 1056 or the CPU, thetelevision set 1050 can have high reliability and sufficiently reducedpower consumption.

EXPLANATION OF REFERENCE

100: transistor, 101: substrate, 102: gate electrode, 103: insulatinglayer, 104: oxide semiconductor layer, 105 a: electrode, 105 b:electrode, 106: insulating layer, 107: insulating layer, 110:transistor, 114: oxide semiconductor layer, 114 a: oxide semiconductorlayer, 114 b: oxide semiconductor layer, 120: transistor, 124: oxidesemiconductor layer, 124 a: oxide semiconductor layer, 124 b: oxidesemiconductor layer, 124 c: oxide semiconductor layer, 150: transistor,151: insulating layer, 152: insulating layer, 160: transistor, 161:transistor, 164: oxide semiconductor layer, 164 a: oxide semiconductorlayer, 164 b: oxide semiconductor layer, 164 c: oxide semiconductorlayer, 164 d: sidewall protective layer, 200: quartz glass substrate,202: dummy substrate, 204: metal oxide film, 210 a: region, 210 b:region, 500: substrate, 501: pixel portion, 502: scan line drivercircuit, 503: scan line driver circuit, 504: signal line driver circuit,510: capacitor wiring, 512: gate wiring, 513: gate wiring, 514: drainelectrode, 516: transistor, 517: transistor, 518: liquid crystalelement, 519: liquid crystal element, 520: pixel, 521: switchingtransistor, 522: driver transistor, 523: capacitor, 524: light-emittingelement, 525: signal line, 526: scan line, 527: power supply line, 528:common electrode, 901: RF circuit, 902: analog baseband circuit, 903:digital baseband circuit, 904: battery, 905: power supply circuit, 906:application processor, 907: CPU, 908: DSP, 910: flash memory, 911:display controller, 912: memory circuit, 913: display, 914: displayportion, 915: source driver, 916: gate driver, 917: audio circuit, 918:keyboard, 919: touch sensor, 1001: main body, 1002: housing, 1003 a:display portion, 1003 b: display portion, 1004: keyboard button, 1021:main body, 1022: fixing portion, 1023: display portion, 1024: operationbutton, 1025: external memory slot, 1030: housing, 1031: housing, 1032:display panel, 1033: speaker, 1034: microphone, 1035: operation key,1036: pointing device, 1037: camera lens, 1038: external connectionterminal, 1040: solar cell, 1041: external memory slot, 1050: televisionset, 1051: housing, 1052: storage medium recording and reproducingportion, 1053: display portion, 1054: external connection terminal,1055: stand, and 1056: external memory.

This application is based on Japanese Patent Application serial no.2012-245992 filed with Japan Patent Office on Nov. 8, 2012, JapanesePatent Application serial no. 2013-016242 filed with Japan Patent Officeon Jan. 30, 2013, and Japanese Patent Application serial no. 2013-056768filed with Japan Patent Office on Mar. 19, 2013, the entire contents ofwhich are hereby incorporated by reference.

1. (canceled)
 2. A transistor comprising: a channel formation regioncomprising an oxide semiconductor, wherein a plurality ofcircumferentially distributed spots are observable in a nanobeamelectron diffraction pattern of the oxide semiconductor.
 3. Thetransistor according to claim 2, wherein a size of a crystalline part ofthe oxide semiconductor is less than or equal to 10 nm.
 4. Thetransistor according to claim 2, wherein a measurement area of thenanobeam electron diffraction pattern is less than or equal to an areawith a diameter of 10 nmφ.
 5. The transistor according to claim 2,wherein the oxide semiconductor comprises indium, gallium, and zinc. 6.The transistor according to claim 2, wherein a size of a crystallinepart of the oxide semiconductor is less than or equal to 5 nm.
 7. Atransistor comprising: a channel formation region comprising an oxidesemiconductor, wherein the oxide semiconductor comprises the channelformation region and a first region in contact with a source electrodeand a second region in contact with a drain electrode, and wherein aplurality of circumferentially distributed spots are observable in ananobeam electron diffraction pattern of each of the channel formationregion, the first region and the second region.
 8. The transistoraccording to claim 7, wherein a measurement area of the nanobeamelectron diffraction pattern is less than or equal to an area with adiameter of 10 nmφ.
 9. The transistor according to claim 7, wherein theoxide semiconductor comprises indium gallium and zinc.
 10. Thetransistor according to claim 7, wherein a size of a crystalline part ofthe oxide semiconductor is less than or equal to 5 nm.
 11. A transistorcomprising: a channel formation region, wherein the channel formationregion comprises an oxide semiconductor comprising a crystalline part,wherein a crystalline peak is not observable in an XRD spectrum withrespect to the oxide semiconductor.
 12. The transistor according toclaim 11, wherein a size of a crystalline part of the oxidesemiconductor is less than or equal to 10 nm.
 13. The transistoraccording to claim 11, wherein the XRD spectrum is obtained byout-of-plane method.
 14. The transistor according to claim 11, whereinthe oxide semiconductor comprises indium gallium and zinc.
 15. Thetransistor according to claim 11, wherein a size of a crystalline partis less than or equal to 5 nm.
 16. A transistor comprising: a channelformation region comprising an oxide semiconductor, wherein the oxidesemiconductor comprising a crystalline part, wherein the oxidesemiconductor comprises the channel formation region and a first regionin contact with a source electrode and a second region in contact with adrain electrode, wherein a crystalline peak is not observable in an XRDspectrum with respect to each of the channel formation region, the firstregion and the second region.
 17. The transistor according to claim 16,wherein the XRD spectrum is obtained by out-of-plane method.
 18. Thetransistor according to claim 16, wherein the oxide semiconductorcomprises indium gallium and zinc.
 19. The transistor according to claim16, wherein a size of a crystalline part of the oxide semiconductor isless than or equal to 5 nm.